Furnfit BWP plywood
Furnfit
Furnfit BWP
Luxury Interior decor
- Grade
- BWP Grade IS:303 2024
- Thickness
- 19mm, 16mm, 12mm, 09mm, 06mm
- Sheet size
- 8'x4'
- Warranty
- 15 years
Product details
- Core: Treated Hardwood
- Face: Gurjan Face c+ Grade
- Resin: E0 BWP Resin
- Thickness tolerance: ± 0.5mm
Applications
- Luxury Interior decor
Not recommended for
Exterior use
Construction & performance
- Construction: Structurally balanced, calibrated plywood with uniform thickness.
- Manufacturing: Four-press technology for strength; vacuum-pressure treatment; chemically treated core veneers.
- Protection: Preservative treated, glue-line treated and borer proof.
- Manufacturer markings: ISO 9001, ISO 14001 and ISO 45001; FSC and CE markings.
- Glue shear after 72 hours boiling: Listed results 1350 N and 1250 N; the table aligns these with minimum individual and average respectively (comparison requirements: 800 N and 1000 N). The printed minimum/average ordering is inconsistent; do not swap or reinterpret the values.
Technical specifications
- Moisture content: 8% (comparison range: 5–15%).
- Dry glue shear strength: Minimum individual 1350 N; average 1500 N (comparison requirements: 1100 N and 1350 N).
- Adhesion to plywood: Excellent (comparison requirement: pass standard).
- Static bending — modulus of rupture (MOR): Along grain 65 N/mm²; across grain 40 N/mm² (comparison requirements: 50 and 30 N/mm²).
- Static bending — modulus of elasticity (MOE): Along grain 8305 N/mm²; across grain 4170 N/mm² (comparison requirements: 7500 and 4000 N/mm²).
- Tensile strength: Along grain 55 N/mm²; across grain 39 N/mm²; combined 94 N/mm² (comparison requirements: 42, 25 and 84.5 N/mm²).
- Wet bending, section A — along grain: MOE average 4650 N/mm² and minimum individual 4100 N/mm² (comparison requirements: 3750 and 3400 N/mm²); MOR average 30 N/mm² and minimum individual 26 N/mm² (comparison requirements: 25 and 22 N/mm²).
- Wet bending, section B: MOE average 3050 N/mm² and minimum individual 2500 N/mm² (comparison requirements: 2000 and 1800 N/mm²); MOR average 25 N/mm² and minimum individual 20 N/mm² (comparison requirements: 15 and 13 N/mm²). The source repeats 'along grain' for section B, so its grain direction is not independently resolved.